Compare Polymers Metal And Ceramics Architecture Essay

Ceramicss are inorganic and nonmetallic stuffs formed from metallic and nonmetallic elements whose interatomic bonds are either ionic or largely ionic. Many of the ceramics desirable belongingss are obtained normally by a high temperature heat intervention. Ceramicss are made up of two or more elements. In a crystalline construction is more complex than that of metals. When the bonding is largely ionic the crystal construction is made up of positively charged metallic ions, cations, negatively charged nonmetallic ions and anions. When the ions are bonded together the overall charge must be impersonal. To hold a stable system the anions in the construction that surround a cation must be in contact with that peculiar ion. There needs to be a ratio of the cation radius to the anion radius for the coordination and apprehension of the constructions geometry. If for illustration there is a deficiency of coordination, the cation would be falsely incased by the anions therefore doing a prostration in its expected structural stableness. There are many different types of constructions exist for ceramics. One crystal construction is the AX type where there are an equal figure of cations and anions. Another crystal construction that exists for ceramics has a different figure of cations and anions but still has a impersonal charge because the ions have different magnitudes of charge is called an AmXp construction. An AmBnXp construction has more than one type of cation, represented by A and B but merely one type of anion. This type of construction is besides seen in close wadding of ions in metals. Imperfections occur in the crystal construction of ceramics really similar to metal structural defects. Defects can happen in each of the two ions of the construction. At any clip there can be cation, anion interstitials, cation or anion vacancies. Most defects or imperfectnesss occur in braces to keep the electroneutrality. A Frenkel defect is a cation vacancy and cation interstitial brace. When a cation and anion vacancy brace occurs they are called a Schottky defect. Ceramicss can besides hold drosss in the crystal construction like metals.Figure 12.21 gives a conventional diagram of the Frenkel and a Schotkey defects ( pg 435 ) .In many instances ceramics tend to be really brickle which can take to ruinous failure with really few marks of weariness. This is due to the fact that ceramics absorb really small energy before they fracture. When ceramics are subjected to a tensile emphasis, they about ever break before any fictile distortion takes topographic point. Fracture occurs because of the formation and extension of clefts perpendicular to the applied burden. Ceramicss have a greater ability to defy compaction than tenseness. The modulus of snap lessenings with more pores in the ceramic stuff. When there are many pores in the stuff they act as emphasis concentrators which expose the stuff to weak part. However, ceramics are really difficult and are good for applications where abradant or crunching action is needed.
Most polymers are organic and are composed of hydrocarbons with interatomic forces that are represented as covalent bonds. Most polymers ironss are rather long and really complex. These long molecules are made up of repetition units which are repeated along the concatenation. The smaller repetition unit is called a monomer. Polymers can be made up of a individual repetition unit, called a homopolymer, or two or more different reiterating units called copolymers.
Polymers by and large have a really big molecular weight. These molecular ironss tend to hold many kinking, bending, and gyrating along with web with adjacent ironss may happen. This causes the result stuff to be really elastic. Polymer ironss can hold side groups which cause different constellations based on which side and with what regularity they bond. They can show a degree of crystallinity similar to the wadding of the molecular ironss to make an ordered atomic array. This crystal construction can be much more complex than metallic crystal constructions. Defects in polymers besides differ from those found in metals and ceramics. Defects in polymers are linked to the concatenation ends because they are somewhat different than the concatenation itself and emerge from the sections of the crystal. Polymers are really sensitive to strive rate, temperature, and chemical nature of the environment. Different polymers can exhibit different emphasis strain behaviour depending on the complexness of the molecular concatenation. Certain polymers display a degree of is brickle where break occurs before elastic distortion which is really similar in the instance of ceramics. Another type of polymers is really similar to metals where elastic distortion takes topographic point foremost followed by giving and fictile distortion. A 3rd type is exhibited by elastomers which have wholly elastic and recoverable distortion. Polymers by and large have a lower modulus of snap and tensile strength so metals. Some Polymers can be stretched up to ten times longer than its original province where metals and ceramics can non easy carry through. Polymers exhibit viscoelasticity at temperatures between where elastic and liquid like behaviours are prevailing. Similar to metals and ceramics, polymers can see weirdo. Creep is a clip dependent factor due to deformation under emphasis or elevated temperature. In both ceramics and polymers, creep depends on clip and temperature. Polymers may be malleable or brickle depending on temperature, strain rate, specimen geometry, and manner of lading which is really similar to the belongingss of metals. Polymers are brickle at low temperatures and have somewhat low impact strengths. Polymers can see weariness under a insistent burden. They are by and large softer than metals and ceramics and unlike metals and ceramics, polymer runing occur over a scope of temperatures alternatively at a specific temperature.

Metallic elements are a stuff made up of metallic elements that are bonded metallically similar common metal. The negatrons are non bound to any peculiar atom making a matrix of ion nucleuss surrounded by many negatrons. They are really good music directors of heat and electricity where as ceramics and polymers are missing. Polymers and metals are both malleable and are non that brickle though metals besides exhibit a degree of plasticity. Ceramicss are really brittle, they tend to fracture under a burden which means they are missing in ductileness. Polymers are the softest stuff due to their complex construction, while ceramics are the hardest but are non really tough because they fracture before fictile distortion occurs. Polymers plastically deform really easy and have the smallest Young ‘s modulus. Ceramicss have the highest value because of their crispness and ne’er reach the point of fictile distortion because they would fracture foremost. The values of Young ‘s modulus for metals fall between those for polymers and ceramics. These three stuffs have diverse constructions and exhibit different degrees of defects.
“ Alloying, ” utilizing the term in the broadest sense.
Simply an metal is a metal compound that consists of 2 or more metal or nonmetallic elements. These combinations of metallic and non metallic elements finally create new compounds that in consequence show superior structural belongingss as compared to the elements by themselves. The type of metal mixtures is extremely dependent on the coveted mechanical belongings of the stuff. Alloying can be applied to metals, ceramics and polymers where in each particular belongingss are desired.
One of the most coveted belongingss of metal metal is the hardenability. A stuff with a high degree of hardness will defy distortion caused by surface indenture or scratch while a stuff with a low hardness degree will deform more easy under similar conditions. The chief factor in a stuff ‘s hardenability is its martensite ( the rate which austenitized Fe C metals are formed when cooled ) besides content and is related to the sum of C in a stuff. With this application of debasing on metals, the stuff can exhibit greater strain and emphasis oppositions every bit good as snap. These belongingss are favourable when covering with building and fabrication procedures.
A ceramic metal is fundamentally a merger of a ceramic with of 2 or more metals. As seen in metal metals, ceramic metals can dwell of dross atoms in a solid province. In ceramic metals an interstitial and substitutional provinces are possible. In an interstitial type, the anion has to be bigger than the dross of the ionic radius. The substitutional dross applies where the dross atom normally forms a cation in the ceramic stuff therefore the host cation will be substituted.Figure 12.23 provides a great ocular representation of interstitial and substitutional types in a ceramic metal ( pg 437 ) .Significantly, to decently accomplish a solid province of solubility for replacing dross atoms, the charge and the ionic size must be as the same as the host ion. If they were different it there would necessitate to be some other manner for the electroneutrality to be maintained within the solid. An easy manner to make this is to make a formation of lattice defects of vacancies or interstitial of both ion types. Cobalt Cr is a perfect illustration of a ceramic metal in which was designed to be used for coronary intercessions therefore because it does non degrade one time placed in the human organic structure.
Polymer alloys consist of two or more different types of polymers in a sense blended together. There are a assortment of additives that can be blended or mixed in with the polymer to make the coveted consequence for the stuff. Polymer additives that support the alteration of its physical belongingss are fillers, plasticisers, stabilizers and of class fire retardents. Fillers are by and large introduced to a polymer, when a greater comprehensive strength and thermic stableness is desired. Making these types of metals are really good because they are by and large really easy to make and utilize in their coveted signifier. Plasticizers help better the flexibleness and stamina of polymers by cut downing the hardness and stiffness of the stuff. They are frequently introduced to polymers that are by and large brickle at room temperature. These additives are particularly utile because they by and large lower the glass passage temperature therefore leting the polymer to hold a extent of bendability. Due to the fact that certain polymers are non resilient to environmental conditions, stabilizers are introduced. They provide stableness and unity against impairment against the mechanical belongingss. The two most common signifiers of environmental impairment are UV exposure and oxidization. A major concern with many polymers is that they are extremely flammable. Fire retardents are introduced to such polymers to cut down the combustibleness of the stuff by interfering with its ability to burn through a gas stage or originating a different burning reaction that generates less heat. This procedure will cut down the temperature that would finally discontinue the combustion procedure.
Kirill Shkolnik
ESG 332 – R01
Exam # 2 ( Question # 2 )
Describe with mention to phase diagrams and disruption theory, how precipitation age hardening can be achieved in aluminium metals.
By and large aluminium is a metal with a low degree of denseness compared to other metals. Due to this low degree of denseness, it conducts electricity and heat better than Cu. Aluminums merely over 1200 grades Fahrenheit which is comparably low to other metals. Due to these simple facts, it seems ideal to bond elements such as Ti, Si, Cu, Zn and other stuffs to amplify aluminiums positive properties. The procedure precipitation age hardening can magnify the alloying of aluminium. This procedure involves supersaturating a solid solution precipitating equally dispersed atoms on the aluminium. This will assist halt the motion of disruptions within the metal construction. The basic construct of disruption is the atomic misalignment of atoms in a additive plane. These atomic misalignments affect a whole series of atoms on a plane. The series of misalign atoms form a line called a disruption line. There are two known types of disruption called the prison guard and border disruption. Screw disruption and border disruption are the primary types of disruptions but require a certain sum of each other to happen. By cut downing the sum of disruptions can radically increase the strength in the metal. The procedure of debasing normally makes a pure stuff harder. The procedure of debasing is holding one metal bond with dross atoms from other stuffs to alter its mechanical belongingss. An debasing procedure called solid solution debasing uses a solution to replace bonds inside the metal. The modification of disruption motion is a major factor for debasing because it can be used to beef up metals. Debasing metals with the precipitation hardening makes the strength of the new stuff stronger as the advancement of the procedure is delayed. The ground for precipitation hardening is sought after is because of its abilities in doing metals stronger.
Aluminum metals can hold precipitation in a really specific manner. Heat intervention occurs when one stuff is heated a supersaturated mixture at a specific stage and so two different stages can be present together. A precipitate signifiers in little pieces throughout the full stuff. When the mixture is at its equilibrium, the forming procedure comes to an terminal. The little pieces of precipitate so spread together to organize one big precipitate. This phase of the precipitate tends to weaken the stuffs cardinal construction. The little pieces of precipitate in the stuff make it harder for disruptions to travel. When strength of the stuff diminishes due to the motion of the precipitate it is called overaging.
There are two things need for heat interventions to be applied.Figure 11.21 provides a graphical representation the relationship between temperature and composing for aluminium and Cu ( pg 402 ) .The Cu stage represented at a shows a supersaturated solid solution in aluminium while the compound that between the two elements is symbolized as? . Interestingly the point M represents the max solubility point at certain temperature and composing in the stuff. Point N represents the solubility bound of a and ( a + ? ) L symbolizes the temperature needed for the solution to go a liquid. If a major sum of solute is made available in the solution, we would hold a precipitation hardened metal. The bound of the solubility curve immensely decreases in concentration as the temperature decreases.
There are two different ways precipitation can happen. One procedure is the usage heat intervention where the solute can be dissolved to organize a solid individual stage solution. This method can be done by heating an metal to a really high temperature.Figure 11.24 shows that the? stage is blended into a stage ( pg 404 ) .Then the metal is cooled where all that is left is a supersaturated a stage. Precipitation heat intervention the ( a + ? ) stage is heated to a specific temperature to let the? stage to precipitate. The metal is cooled and the hardness of the metal is determined by clip. A logarithmic map a comparing with strength and clip proves the dependance of temperature and strength.
Kirill Shkolnik
ESG 332 – R01
Exam # 2 ( Question # 3 )
Describe what is meant by the term “ glass passage temperature ” and exemplify your reply from polymer and ceramic point of position.
Typically a glass passage temperature is where a noncrystalline signifier of a polymer or a ceramic is cooled and transforms from a super cooled liquid into a glass. A ceramic or a glassy stuff is a noncrystalline stuff that becomes progressively more syrupy when it is cooled. Due to the fact that glassy stuffs are noncrystalline there is no definite temperature when the liquid will transform into a solid. Though, it is besides of import to observe that in noncrystalline stuffs the specific volume is dependent on temperature and will diminish with the temperature. The glass passage temperature displays a decrease in the rate at which the particular volume decreases with temperature. When the temperature is below this value, the stuff is in a ceramic from and straight above this point the stuff is considered a supercooled liquid. The glass passage temperature occurs in both glassy and semicrystalline polymers, but non in crystalline stuffs. As certain molecular ironss in noncrystalline stuffs temperature bead due to miss of gesture the glass temperature passage occurs. Basically glass passage is the clip in which a steady transmutation occurs from the liquid province to a somewhat rubberlike province and so to the concluding more stiff solid stuff. The glass passage temperature is the province in which the stuff goes from its rubbery to stiff province.
This passage can take topographic point in both waies. As a polymer for illustration is cooled to a stiff solid, it can be heated and undergo the same passage in contrary. As the stuff undergoes all of these alterations its belongingss change from province to province. Some stuffs can see greater alteration include the stiffness, heat capacity, and the coefficient of thermic enlargement for the stuff during this passage. The glass passage temperature besides acts as a bound boundary for applications of polymers and polymer matrix like constituents. If this temperature is beyond the stuff threshold, it will no longer suit the coveted belongingss the undertaking had called for and the application would be useless. The molecules that had been frozen in topographic point below the will both revolve and interpret at the temperatures above. Molecular features have an impact on the concatenation ‘s stiffness and will in bend affect the glass passage temperature for the stuff.
Some molecular features that can do the concatenation ‘s flexibleness to be reduced and the glass passage temperature to increase that include bulky side groups on the molecular concatenation. Besides these features can impact polar atoms or groups of polar atoms on the side of the molecular concatenation, dual bonds, and aromatic groups. The glass passage temperature will besides increase as the molecular weight of the stuff additions. Branching besides influences the of a stuff, many subdivisions will diminish the ironss mobility and addition, a lower denseness of subdivisions will do the to diminish as the molecular ironss will hold a freer scope of gesture.
Crosslinks can happen in glassy polymers and can impact, they cause the decrease of gesture and hence addition. If there are excessively many crosslinks occur in the stuff, the molecular gesture would be so limited that glass passage may non happen. It can be understood that many of the same molecular features which affect the glass passage temperature besides affect the thaw passage temperature. The two are affected in such a similar mode that is normally someplace between 0.5 to 0.8 times the runing passage temperature.Figure 15.19 demonstrates this mathematic relationship ( pg 548 ) .Both ceramic and polymers have a glass passage temperature. A glass can be referred to by several different names ; such as vitreous solid, an formless solid or glassy solid. An formless solid has the mechanical belongingss of a solid, but does non hold long scope molecular order where they are in gesture at a really slow rate that it be considered stiff for regular intents. When glassy stuffs have been supercooled below the glass passage temperature they will take on features similar to those of a crystalline solid. This solid will go stiff with an increased hardness and will be more brickle. However, if a glassy stuff is heated to above its glass passage temperature it will go softer and many of the intermolecular bonds will interrupt leting the stuff to flux at an increasing fluid viscousness. A polymer below the glass passage temperature is more stiff, but as it enters its glass passage stage, the stuff becomes more rubbery as its viscousness additions. The polymer can come in its glass passage at a lower temperature when critical factors that normally affect the gesture of the molecules in the stuff are non all present.
When molecular weight of a polymer additions, the glass passage temperature will besides increase. Many factors that increase the the gum elastic gasket would non make its occupation decently.
Polymers can exhibit the undermentioned constructions: formless, semi-crystalline and crystalline. Describe these constructions and explicate how the mechanical belongingss may be influenced by these structural signifiers for a polymer of the same chemical expression.
Polymers can develop formless, semi-crystalline and crystalline constructions of the same chemical expression. Polymers can be as liquids, semi solids, or solids related to the crystal constructions severally. However each of these constructions exhibit a assortment of different mechanical belongingss. The crystallinity of a polymer depends on the intermolecular secondary bonding which will to a great extent act upon the extent of any mechanical belongings of the polymer.
The tensile strength, elastic modulus and compaction strength of a crystalline construction will be stronger than a semicrystalline construction and significantly stronger than formless type construction.
For a crystalline construction the molecular ironss of the polymer are tightly packed together in an organized atomic group which take up infinite and will impact the polymers mechanical belongingss. These crystalline constructions are to a great extent influenced by the glass passage temperature. Besides the isomer and chemical expression lays out important factors that will be really of import in the formation of the bulk stuff construction.
From certain big bulky functional groups there becomes an at hand hinderance that will suppress the motion capableness of a molecule. This procedure will increase the energy demand for any stage alteration. The result of this procedure is a greater passage temperature. This new temperature passage will increase the opportunities for the formation of a crystalline construction. The ground for this is and clip p before the stuff becomes a disorganised liquid and requires a longer clip for the molecules to set up themselves decently. When polymers have many subdivisions the weaker the stuff will be, even though crystalline constructions are stronger than less ordered stuffs.Figure 15.18 demonstrates the alteration in these structural provinces when specific volume and temperature are compared ( pg 546 ) .Pure polymers have a really little runing point scopes and bond strength. Doped polymers and polymer metals will by and large hold wider runing point scopes. The procedure of ramification will diminish the strength of a polymer, which would continuously diminish the thaw point temperature. Though, the act of ramifying on to a great extent heavy subdivisions will diminish molecule mobility. Besides within this procedure the molecular weight is affected every bit good.
Kirill Shkolnik
ESG 332 – R01
Exam # 2 ( Question # 4 )
How are T-T-T and C-C-T diagrams used to plan heat intervention agendas for field C steels.
Time-Temperature-Transformation or T-T-T and uninterrupted chilling transmutation or
C-C-T are used for heat intervention agendas for field C steel. T-T-T are normally known as an isothermal transmutation diagrams can demo the alteration of different stages at certain temperatures. C-C-T can be used to cipher percent transmutation against the logarithm map through clip.
The usage the isothermal transmutation and uninterrupted chilling transmutation diagrams can be used to develop a heat intervention for field C steels. These diagrams will back up the apprehension of C steels through stage diagrams. When a construction is heat treated, its chilling procedure helps retain its construction. This procedure can be analyzed through T-T-T.Figure 10.13 displays a graphical representation of temperature against clip with a 3rd dimension with the per centum of the steel metal transformed to pearlite ( pg 326 ). The apprehension of a rapid chilling metal sully depends on the apprehension and application of heat intervention. It is understood that isothermal transmutations do non alter in temperature but uninterrupted chilling transmutation diagrams do. C-C-T and T-T-T display the same dimensions but over a larger spectrum of clip and temperature.Figure 10.28 shows different signifiers of steel metals ( pg 338 ) .A stuff that has been cooled to a temperature somewhat below its eutectoid temperature, and isothermal transmutation is maintained for an drawn-out period of clip, interestingly it can non be depicted on T-T-T diagrams in spheroid signifiers.

Don't use plagiarized sources. Get Your Custom Essay on
Compare Polymers Metal And Ceramics Architecture Essay
Just from $13/Page
Order Essay

Calculate the price of your paper

Total price:$26
Our features

We've got everything to become your favourite writing service

Need a better grade?
We've got you covered.

Order your paper
Live Chat+1(978) 822-0999EmailWhatsApp